Phaetus nozzle 0.4 tungsten carbide
Phaetus nozzle 0.4 tungsten carbide
Phaetus Tungsten Carbide Nozzle has very high wear resistance and a nearly unlimited service life.
It is therefore "one nozzle for all types of filament" - from regular PLA to high temperature filaments such as PEEK and even carbon fiber filaments.
Hardness (Mohs): 9
Maximum printing temperature: 550℃
Thermal conductivity: 130W/mk
Coefficient of expansion: 4.7 μm/m℃ More
Manufacturer: PhaetusProduct code: 590 Shipping and Payment
Phaetus Tungsten Carbide Nozzle has very high wear resistance and a nearly unlimited service life.
It is therefore "one nozzle for all types of filament" - from regular PLA to high temperature filaments such as PEEK and even carbon fiber filaments.
Hardness (Mohs): 9
Maximum printing temperature: 550℃
Thermal conductivity: 130W/mk
Coefficient of expansion: 4.7 μm/m℃ More
Manufacturer: PhaetusProduct code: 590 Shipping and Payment
Super Wear-Resistance
Using the world’s leading ultra-high hardness tungsten carbide (hardness > 2700Hv (up to 2900Hv)), super wear resistance ensures long-term printing without wearness of nozzle hole and tip flat.
High Temperature Performance
Composed of tungsten carbide and copper alloy with super hardness and excellent conductivity, maximum printing temperature can be 550℃.
Low Pushing Force
Tungsten Carbide Nozzle with high purity more than 99.98% and high thermal performance keeps an even temperature of nozzle tip during printing, thus guaranteeing a stable extrusion.
Faster Speed
Due to the high thermal performance of the nozzle in general, the printing speed can be pushed even further without sacrificing the quality. Unique passageway in the nozzle improves the flow rate at the inner hole faster.
Low Friction
The whole nozzle is applied with DLC coating . Surface friction coefficient is as low as 0.05 which makes the nozzle with clean printing, without plastic sticking to it.
DLC coating
- Friction coefficient is only 0.05, effectively avoiding molten plastic sticking to the nozzle;
- Coating thickness 2.0μm, without effects on any dimension accuracy;
- Maintaining good lubrication and wear-resistance up to 300℃;
- Strong adsorption capacity, coating hardness HV2200;
- Stable chemical properties, non-toxic, non-corrosive and insoluble in other solvents.
Applicable filament
One Nozzle , All Materials
From conventional printing with PLA to PEEK, even to Carbon Fiber reinforced materials, Tungsten Carbide Nozzle can easily handle with long time printing with any material.
Product features
- Nozzle diameter: 0.4 mm
- Filament diameter: 1.75 mm
- Thread: M6
- Color: black
- Material: tungsten carbide
- Min. Orifice Diameter: φ0.25
- Tolerance: ±0.01mm
- Inner Hole Roughness: ≤Ra0.4μm
- Concentricity: ≤0.02mm
- Hardness (Mohs): 9
- Maximum Printing Temperature: 550℃
- Thermal Conductivity: 130W/mk
- Expansion Coefficient: 4.5μm/m℃
Type | Thermal Conductivity (W/mk) | Hardness (Mohs) | Maximum printing temperature | Thermal expansion Coefficient (μm/m℃) | Applicable materials |
---|---|---|---|---|---|
Brass nozzle | 105 | 3.0 | 300 | 18 | Common materials such as PLA, PET-G, ABS, ASA, TPU, PA etc. |
Stainless Steel Nozzle | 17 | 5.0 | 350 | 6.0 | |
Copper Plated Nozzle | 330 | 6.0 | 500 | 16.7 | PEEK, PEI and all abrasive filaments containing glass or carbon fibre and wood or metal powder. |
Hardened Steel Nozzle (Blackened) | 22 | 7.8 | 450 | 8.0 | |
Hardened Steel Nozzle (Nickel Plated) | 20 | 7.8 | 450 | 8.0 | |
Hardened Steinless Steel Nozzle | 18 | 8.0 | 450 | 6.0 | |
Ruby Nozzle | 45 | 9.0 | 550 | 5.3 | All materials |
Tungsten Carbide Nozzle | 130 | 9.0 | 550 | 4.5 | All materials |